ETCHED GLASS FILMS
Polymeric Etched Glass Films (80μ) with sand blasting and frosty effect surfaces. Coated with a humidity resistant solvent acrylic adhesive. The Etched Glass Films are suitable for mid- to long-term application on glass and mirrors as well as to achieve a sand blasting or frosty effect on transparent plastic sheets. Printable with ECO-Solvent, Solvent, Latex and UV inks.
Outdoor durability: 5-7 years
ETCHED GLASS FILMS |
|
POLI-ETCH 5052 SILVER FROSTY | |
---|---|
Carrier | polymeric PVC, highly stabilized, calendered |
Thickness | 80 μm +/- 5 % |
Adhesive | clear solvent acrylic, permanent |
Adhesion | 7,5 N/cm +/- 5% |
Liner | one-sided Clay-coated silicone paper (143 g/m2) |
Application | Polymeric PVC film (translucent) with a frosty effect surface. Coated with a clear solvent acrylic adhesive. Suitable for wet and dry application. Especially developed to achieve a sand blasting or frosty effect on glass and mirrors as well as transparent plastic sheets. The PVC film possesses a minimal shrinkage performance and is suitable for mid- to long-term inside and outside application. Printable with ECOSolvent, Solvent, Latex and UV printers. |
Dimensions | 50 m x 1220 / 1372 / 1524 mm |
ICC profiles | Hewlett-Packard_L25500_6d987c.oml / Mimaki_JV33-160_251d92.oml / Mutoh_VJ1624-3A_b97270.oml / Seiko_CP_W64S_bf22e5.oml / |
Datasheets | POLI-ETCH_5052_Silver_Frosty_GB.pdf |
ETCHED GLASS FILMS |
|
POLI-ETCH 5053 DUSTY | |
---|---|
Carrier | polymeric PVC, highly stabilized, calendered |
Thickness | 80 μ +/- 5 % |
Adhesive | transparent solvent acrylic, permanent |
Adhesion | 7,5 N/cm +/- 5% |
Liner | one-sided Clay-coated silicone paper (143 g/m2) |
Application | Polymeric PVC film (translucent) with a frosty effect surface. Coated with a clear micro-structured solvent based acrylic adhesive. Suitable for wet and dry application. Especially developed to achieve a sand blasting or frosty effect on glass and mirrors as well as transparent plastic sheets. The PVC film possesses a minimal shrinkage performance and is suitable for mid- to long-term inside and outside application. Printable with ECO-Solvent, Solvent, Latex and UV printers. |
Dimensions | 50 m x 1372 mm |
ICC profiles | Hewlett-Packard_L25500_469493_01.oml / Mimaki_JV33-160_96942d_01.oml / Mutoh_VJ1624-3A_dac650_01.oml / Seiko_CP_W64S_d67f26_01.oml / |
Datasheets | POLI-ETCH_5053_DUSTY_GB.pdf |
ETCHED GLASS FILMS |
|
POLI-ETCH 5054 SILVER | |
---|---|
Carrier | polymeric PVC, highly stabilized, calendered |
Thickness | 80 μm +/- 5 % |
Adhesive | clear acrylic dispersion, permanent |
Adhesion | 3,5 N/cm +/- 5% |
Liner | one-sided Clay-coated silicone paper (135 g/m2) |
Application | Polymeric PVC film (translucent) with a frosty effect surface. Coated with a special acrylic dispersion adhesive. No silvering effect. Suitable for wet and dry application. Especially developed to achieve a sand blasting or frosty effect on glass and mirrors as well as transparent plastic sheets. The PVC film possesses a minimal shrinkage performance and is suitable for mid- to long-term inside application. Printable with ECOSolvent, Solvent, Latex and UV printers. |
Dimensions | 50 m x 1050 mm / 1220 mm / 1372 mm |
ICC profiles | Hewlett-Packard_L25500_6d987c_01.oml / Mimaki_JV33-160_251d92_01.oml / Mutoh_VJ1624-3A_b97270_01.oml / Seiko_CP_W64S_bf22e5_01.oml / |
Datasheets | POLI-ETCH_5054_Silver_GB.pdf |
ETCHED GLASS FILMS |
|
POLI-ETCH 5055 SILVER FROSTY AIR FREE | |
---|---|
Carrier | polymeric PVC, highly stabilized, calendered |
Thickness | 80 μm +/- 5 % |
Adhesive | clear micro-structured solvent acrylic, permanent |
Adhesion | 7,5 N/cm +/- 5% |
Liner | PE-coated silicone paper (145 g/m2) |
Application | Polymeric PVC film (translucent) with a frosty effect surface. Coated with a clear micro-structured solvent based acrylic adhesive. Suitable for dry application. Especially developed to achieve a sand blasting or frosty effect on glass and mirrors as well as transparent plastic sheets. The PVC film possesses a minimal shrinkage performance and is suitable for mid- to long-term inside and outside application. Printable with ECO-Solvent, Solvent, Latex and UV printers. |
Dimensions | 50 m x 1220 / 1372 / 1524 mm |
ICC profiles | Hewlett-Packard_L25500_469493_04.oml / Mimaki_JV33-160_96942d_04.oml / Mutoh_VJ1624-3A_dac650_04.oml / Seiko_CP_W64S_d67f26_04.oml / |
Datasheets | POLI-ETCH_5055_Silver_Frosty_Air_Free_GB.pdf |
ETCHED GLASS FILMS |
|
POLI-ETCH 5057 SILVER AIR FREE | |
---|---|
Carrier | polymeric PVC, highly stabilized, calendered |
Thickness | 80 μm |
Adhesive | clear, micro-structured Acrylic Dispersion, permanent |
Adhesion | 3,5 N/cm |
Liner | two-sided PE-coated silicone paper (145 g/m2) |
Application | Polymeric PVC film (translucent) with a frosty effect surface. Coated with a special micro-structured acrylic adhesive enables an easy repositioning during the application. No silvering effect. Suitable for wet and dry application. Especially developed to achieve a sand blasting or frosty effect on glass and mirrors as well as transparent plastic sheets. The PVC film possesses a minimal shrinkage performance and is suitable for mid- to long-term inside application. Printable with ECOSolvent, Solvent, Latex and UV printers. |
Dimensions | 50 m x 1050 mm / 1220 mm / 1372 mm |
ICC profiles | Hewlett-Packard_L25500_6d987c_03.oml / Mimaki_JV33-160_251d92_03.oml / Mutoh_VJ1624-3A_b97270_03.oml / Seiko_CP_W64S_bf22e5_03.oml / |
Datasheets | POLI-ETCH_5057_Silver_Air_Free_GB.pdf |